Description of High Purity Furnace Refractory Bricks Silicon Carbide Bricks For Furnaces
Silicon carbide bricks are refractory products made of silicon carbide as the main raw material. Silicon carbide content is 72%~99%. Generally, black silicon carbide (with more than 96% SiC content) is used as raw material, with binder (or without binder) added, and is prepared through batching, mixing, molding, firing and other processes. The main crystalline phase is silicon carbide. The main varieties are oxide bonded silicon carbide bricks, carbon bonded silicon carbide bricks, nitride bonded silicon carbide bricks, self bonded silicon carbide bricks, recrystallized silicon carbide bricks and semi silicon carbide bricks.
Features of Silicon Carbide Refractory Brick
1.Good thermal conductivity
2.Good high temperature strength
3.Wear resistant and erosion resistant
4.Boa resistência ao choque térmico
5.Good corrosion resistance
6.Good oxidation resistance.
Applications of Silicon Carbide Brick:
ilicon carbide bricks find applications in industries such as metallurgy, ceramics, vidro, cimento, and other high-temperature processes. They are used in areas of furnaces, kilns, and other high-temperature equipment.
Technical Parameter of Silicon Carbide Brick:
| Item | Bonding Type | |||||||
| Argila | Mullite | SiO2 | Si3N4 | Sialon | β-SiC | R-SiC | Siliconizing reaction | |
| SiC % | ＞85 | ＞70 | ≥90 | ≥72 | ≥71 | ≥94 | ≥99 | ≥80 |
| Si3N4 % | / | / | / | ≥20 | / | / | / | / |
| Al2O3 % | / | / | / | / | ≥5 | / | / | / |
| Si % | / | / | / | / | ≥5.5(N) | / | / | 12~18 |
| Bulk Density g/cm3 | 2.5~2.6 | 2.55~2.65 | 2.6~2.7 | ≥2.65 | ≥2.65 | ≥2.63 | ≥2.65 | ≥3.0 |
| Apparent porosity % | ≤20 | ≤16 | ≤15 | ≤16 | ≤16 | ≤17 | ≤15 | ≤0,5 |
| Flexural strength at room temperature MPa | ≥20 | ≥25 | ≥25 | ≥45 | ≥45 | ≥30 | ≥90 | ≥220 |
| Flexural strength at high temperature MPa 1400℃ | / | / | / | ≥45 | ≥45 | ≥30 | ≥90 | ≥240 |
| Cold Crushing strength MPa | ≥100 | ≥100 | ≥120 | ≥160 | ≥150 | ≥140 | ≥300 | ≥800 |